Ag-Nb-Pt Bazlı SCR Katalizör Karakterizasyonu

Basit Öğe Kaydı
dc.contributor.authorKeskin, Ali
dc.contributor.authorYaşar, Abdulkadir
dc.contributor.authorKeskin, Zeycan
dc.contributor.authorAkar, M. Atakan
dc.contributor.authorReşitoğlu, İ. Aslan
dc.contributor.authorÖzarslan, Himmet
dc.contributor.authorAydın, Kadir
dc.date.accessioned2025-03-16T12:43:04Z
dc.date.available2025-03-16T12:43:04Z
dc.date.issued2018
dc.departmentTarsus Üniversitesi
dc.description.abstractSeçici Katalitik İndirgeme (SCR), dizel motorlarda NOx emisyonlarını azaltmak için kullanılan bir emisyon kontrol sistemidir. Bu çalışmada, SCR sistemi için gümüş esaslı katalizörün sentezlenmesi deneysel olarak incelenmiştir. Bu amaçla, kordiyerit (2Al2O3-5SiO2-2MgO) yapısını daldırma yöntemiyle kaplamak amacıyla gümüş nitrat (AgNO3), niyobyum (V) klorür (NbCl5) ve tetra amin platin (II) nitrat (Pt (NH3)4 (NO3)2) katalizörleri kullanılmıştır. Katalizörün kimyasal ve fiziksel özelliklerini belirlemek için XRF, SEM ve BET analizleri gerçekleştirilmiştir. Sonuçlar, kaplama malzemelerinin gözeneklerin tüm yüzeyine nüfuz ettiğini göstermiştir. Üretilen katalizör ve kordieritin BET yüzey alanlarının sırasıyla 0,2918 m2/g ve 0,4568 m2/g olduğu belirlenmiştir. Yüzey alandaki azalmanın, yüksek sinterleme sıcaklığında meydana gelen kimyasal reaksiyonlarla kristalizasyon artışına bağlı olduğu düşünülmektedir. Ayrıca, XRF analizi sonuçları, kordierit yapısındaki Ag içeriğinin %0,03 olmasına karşın katalizörde Ag, Pt ve Nb içeriğinin sırasıyla %3,67, %0,19 ve %0,12 oranlarında olduğunu ortaya koymuştur. 
dc.description.abstractSelective Catalytic Reduction (SCR) is an emission control system used in diesel engines to reduce NOx emissions. In this study, synthesized of catalyst for SCR system was investigated as experimentally. For this purpose, silver nitrate (AgNO3), niobium (V) chloride (NbCl5) and tetra amine platinum (II) nitrate (Pt(NH3)4(NO3)2) were used to coat the cordierite (2Al2O3-5SiO2-2MgO) structure with impregnation method. X-ray Fluorescence (XRF), Scanning Electron Microscope (SEM) and Brunauer, Emmett, and Teller (BET) analyzes were carried out in order to determine the chemical and physical properties of the catalyst. Results showed that the coating materials penetrate the entire surface of the pores. It was also determined that the BET specific surface areas of the produced catalyst and cordierite are 0.2918 m2/g and 0.4568 m2/g, respectively. The reduction of surface area could be attributed to the increment of crystallization with chemical reactions occurred at the high sintering temperature. Besides, XRF analysis results demonstrated that content of Ag, Pt and Nb in the in the catalyst was found to be 3.67%, 0.19% and 0.12%, respectively, whereas Ag content in cordierite structure was 0.03%. 
dc.identifier.doi10.21605/cukurovaummfd.521723
dc.identifier.issn1019-1011
dc.identifier.issn2564-7520
dc.identifier.issue4
dc.identifier.startpage42614
dc.identifier.urihttps://doi.org/10.21605/cukurovaummfd.521723
dc.identifier.urihttps://hdl.handle.net/20.500.13099/519
dc.identifier.volume33
dc.language.isoen
dc.publisherÇukurova Üniversitesi
dc.relation.ispartofÇukurova Üniversitesi Mühendislik-Mimarlık Fakültesi Dergisi
dc.relation.publicationcategoryMakale - Ulusal Hakemli Dergi - Kurum Öğretim Elemanı
dc.rightsinfo:eu-repo/semantics/openAccess
dc.snmzKA_DergiPark_20250316
dc.subjectKatalizör
dc.subjectXRF
dc.subjectSEM
dc.subjectBET
dc.subjectSCR
dc.subjectEgzoz emisyonları
dc.subjectCatalyst
dc.subjectXRF
dc.subjectSEM
dc.subjectBET
dc.subjectSCR
dc.subjectExhaust emissions
dc.titleAg-Nb-Pt Bazlı SCR Katalizör Karakterizasyonu
dc.title.alternativeCharacterization of SCR Catalyst Based Ag-Nb-Pt
dc.typeArticle

Dosyalar

Koleksiyon

Öksüz Yayınlar