    A study of the cell morphology and mechanical properties of bumper material PP-T-EPDM composite foam
    (Sage Publications Ltd, 2023) Yetgin, Salih Hakan; Unal, Huseyin
    In this study, cellular polypropylene based composite foams were prepared using an universal injection moulding machine. The chemical foaming agent was added to neat polypropylene (PP) polymer, talc filled polypropylene (PP-T) composite and talc filled polypropylene/ethylene-propylene-diene blend (PP-T-EPDM) composite materials at the ratio of 1% and 2% by weight. The influence of foaming agent content on the mechanical and cellular properties of both neat PP polymer and PP composites was investigated. The results showed that the tensile strength, tensile modulus, impact strength, hardness, cell diameter, foam density and viscosity values and skin layer thickness decreased while volume expansion ratio increased with the increment in chemical blowing agent content.
  • [ X ]
    Öğe
    Analysis of Tribological Properties of Tin Powder Filled Polypropylene Composites with Taguchi Method
    (Polymer Soc Korea, 2022) Gulesen, Mustafa; Kacal, Alaattin; Unal, Huseyin; Yetgin, Salih Hakan
    The tribological behavior of polypropylene polymer composites filled with Tin powder as fillers was studied using a pin-on-disc wear test rig at dry sliding conditions. The influence of wear process parameters like materials type (MT), applied load (AL), and sliding speed (SS) on the coefficient of friction (CoF) and specific wear rate (SWR) were investigated. A plan of experiments based on Taguchi technique performed to acquire data in a controlled way. An orthog-onal array and analysis of variance (ANOVA) employed to investigate the influence of process parameters on the wear of these composites. The results showed that Tin powder's addition as filler materials in polypropylene composites increased the specific wear resistance of the polypropylene composite significantly.
  • [ X ]
    Öğe
    BURÇ, CONTA VE RULMAN UYGULAMALARI İÇİN SAF POLİ-TETRA-FLOR-ETİLEN VE BRONZ TAKVİYELİ POLİ-TETRA-FLOR-ETİLEN KOMPOZİTİN TRİBOLOJİK PERFORMANSLARININ KARŞILAŞTIRILMASI
    (2024) Maslavi, Ahmet; Ünal, Hüseyin; Yetgin, Salih Hakan
    Bu çalışmada, endüstrinin çeşitli sektörlerinde makinelerde sıkça kullanılan hidrolik piston contaları, salmastra ve keçeler gibi polimerlerden üretilen malzemelerin tribolojik performansları incelenmiştir. Tribolojik çalışmada saf poli-tetra-flor-etilen (PTFE) polimeri ile ağırlık olarak %25 oranında bronz takviyeli poli-tetra-flor-etilen (PTFE/25bronz) kompozit kullanılmış ve her iki malzemenin tribolojik performansları karşılaştırılmıştır. Tribojik deneyler disk üzerinde pim olacak şekilde dizayn edilmiş aşınma cihazında gerçekleştirilmiştir. Tribolojik deneyler 30N-150N yük aralığında ve 1.0 m/s kayma hızında yapılmıştır. Deneylerde sürtünme katsayısı, aşınma hacmi, pim/disk yüzey sıcaklıkları ve spesifik aşınma oranı ölçülmüştür. Çalışma sonucunda PTFE/25 bronze kompozitin sürtünme katsayısı, pim/disk yüzey sıcaklığı ve aşınma oranı saf PTFE’ye daha düşük olduğu tespit edilmiştir. PTFE polimerine %25 bronz ilavesi kompozitin spesifik aşınma oranında önemli oranda azalmaya sebep olmuştur. Taramalı elektron mikroskobu ve optik mikroskop kullanılarak numunelerin aşınma yüzey mikroyapı incelemeleri gerçekleştirilmiştir. Saf PTFE polimerinde abrazif aşınma, PTFE/bronz kompozitinde ise adhezif aşınma mekanizması gözlenmiştir.
  • [ X ]
    Öğe
    Cam Bilya Katkılı Poliamit 6.6 Kompozitlerin Mekanik ve Mikroyapı Özelliklerine Cam Bilya Katkı Oranının Etkisi
    (2023) Ünal, Hüseyin; Yetgin, Salih Hakan; Ünal, Veysel Furkan
    Bu çalışma, katkısız poliamit 6.6 (PA6.6) ile ağırlıkça %10-20-30 oranlarında cam bilya içeren poliamit 6.6 kompozitlerin mekanik ve mikroyapı özelliklerini incelemek için yapılmıştır. Cam bilya katkılı Poliamit 6.6 kompozitler, endüstriyel tip ikiz vidalı bir ekstrüder makinesinde granül formda üretilmiştir. Deneylerde kullanılan mekanik test numuneleri geleneksel enjeksiyon makinesi kullanılarak basılmıştır. Çalışma sonucunda, PA6.6 polimerine ilave edilen cam bilya çekme dayanımını, kopmadaki uzama miktarını ve charpy darbe dayanımını azaltırken elastiklik modülünü artırmıştır. Mikroyapı incelemeleri için taramalı elektron mikroskobu (SEM) kullanılmıştır. Mikroyapı incelemelerinde cam bilyaların polimer matris içinde homojen olarak dağıldığı gözlenmiştir.
  • [ X ]
    Öğe
    Cam Elyaf Takviyeli Poli-amit 6 Kompozitler ile Poliamit-6 Polimerinin %30 Cam Elyaf Takviyeli Poli-amit 6 Kompozitine Karşı Aşınma ve Sürtünme Davranışları
    (2024) Saylan, Tacettin; Ünal, Hüseyin; Yetgin, Salih Hakan
    Bu çalışmada, katkısız poli-amit polimeri ile ağırlık olarak farklı oranlarda (%10-%20-%30) kısa cam elyaf (CE) takviyeli poli-amit kompozitlerin aşınma ve sürtünme davranışları incelenmiştir. Aşınma deneyleri %30 kısa cam elyaf takviyeli poli-amit 6 (PA6+%30CE) kompozit diske karşı kuru ortam şartları altında gerçekleştirilmiştir. Cam elyaf takviyeli PA6 esaslı kompozitler önce ikiz vidalı bir ekstruderde granül formunda üretilmiş ardından enjeksiyon makinasında aşınma test numuneleri basılmıştır. Aşınma testleri 0,5 m/s kayma hızı, 20-30-40 N yükte ve 1500 m kayma mesafesinde yapılmıştır. Deneyler, pim-disk aşınma test cihazı kullanılarak ortam sıcaklığında gerçekleştirilmiştir. Deneyler sonucunda, katkısız PA6 polimerinin sürtünme katsayısı ve aşınma oranı uygulanan yük ile artış göstermiştir. Kısa CE takviyeli PA6 kompozitlerin sürtünme katsayısı da artarken aşınma oranında ise pek artış gözlenmemiştir. En düşük sürtünme katsayısı ve aşınma oranı %30 CE takviyeli PA6 kompozitinde elde edilmiştir. PA6 polimerine %30 oranında CE takviyesi ile kompozitin aşınma direnci katkısız PA6 polimerine göre en az %48 oranında artmıştır.
  • [ X ]
    Öğe
    Cam Elyaf Takviyeli Poli-fital-amit Polimer Kompozitlerin Aşınma ve Sürtünme Performanslarının Araştırılması
    (2024) Hatipogğlu, Gizem; Ünal, Hüseyin; Yetgin, Salih Hakan
    Endüstrinin birçok alanında üretim makinelerinde hareket iletiminde polimer ve polimer esaslı kompozit malzemelerden imal edilmiş dişliler kullanılmaktadır. Uygun malzeme çiftlerinin seçimi dişli mekanizmalarının çalışma ömrünü belirlemektedir. Yüksek performanslı poli-fital-amit (PPA) polimeri ve PPA kompozitleri makine elemanlarının ömrünü artırabilecek malzemelerdendir. Bu çalışmada, katkısız poli-fital-amit polimeri ile ağırlık olarak %30 oranında cam elyaf takviyeli poli-fital-amit (PPA/%30GF) kompozitinin aşınma ve sürtünme performansları incelenmiştir. Aşınma deneyleri çelik diske karşı kuru ortam şartları altında gerçekleştirilmiştir. Cam elyaf takviyeli PPA kompoziti ikiz vidalı endüstriyel bir ekstruderde granül olarak üretilmiş ardından enjeksiyon makinesinde aşınma test numuneleri basılmıştır. Aşınma testleri 0,5 ve 1,0 m/s kayma hızlarında, 20 N, 30 N ve 40 N yükler altında yapılmıştır. Deneyler, pim-disk aşınma test cihazı kullanılarak ortam sıcaklığında gerçekleştirilmiştir. Aşınma testleri sonucunda, cam elyaf takviyeli PPA kompozitin sürtünme katsayısı ve aşınma oranının katkısız PPA polimerine göre daha düşük olduğu belirlenmiştir. Uygulanan yükün artması ile sürtünme katsayısı artarken hızın artması ile sürtünme katsayısı azalmıştır. Aşınma oranı ise uygulanan yük ve kayma hızının artması ile artmıştır. Uygulanan tribolojik test çalışma şartlarında % 30 oranında cam elyaf takviyeli poli-fital-amit katkısız PPA’ya göre ortalama da en az 5 kat dirençli olduğu tespit edilmiştir.
  • [ X ]
    Öğe
    Cam Elyaf, Cam Bilya ve EPDM katkılı Poliamit-6 Hibrit Kompozitlerin Mekanik Performanslarının Belirlenmesi
    (2022) Ünal, Hüseyin; Yetgin, Salih Hakan; Özsarikaya, Bilal
    Otomotiv, beyaz eşya, savunma sanayi, uçak ve uzay sanayinde kullanılan bazı parçaların yüksek mukavemetli olmasının yanında aynı zamanda tok ve darbe dayanımlı olması da istenir. Bu çalışmada, ana matris malzeme olarak mühendislik polimerleri sınıfında yer alan poliamit 6 (PA6) polimeri kullanılmıştır.Katkısız PA6 polimeri ile ağırlık olarak %5 oranında cam bilya (CB) katkılı poliamit 6 (PA6-5CB), %15 oranında cam elyaf (CE) takviyeli poliamit 6 (PA6-15CE) ve %5CB/%15CE/%4 Etilen-Propilen-Dien-Monomer (EPDM) katkılı poliamit 6 (PA6-5CB-15CE-4EPDM) hibrit kompozitlerin mekanik performansları araştırılmıştır. Poliamit-6 esaslı polimer kompozitler önce ikiz vidalı ekstrüderde granül formda üretilmiş sonrasında ise enjeksiyon kalıplama yöntemi ile test numuneleri üretilmiştir. Enjeksiyon kalıplama yöntemi ile ASTM standartlarına uygun olarak çekme, darbe ve eğme numuneleri üretilmiştir. Çalışma sonucunda, PA6 polimerine ilave edilen %5 oranında cam bilya çekme mukavemetini %2 oranında artırırken elastiklik modülünü etkilememiştir. PA6 polimerine ilave edilen %15 oranındaki cam elyaf ise çekme mukavemetini %51.5 oranında, elastiklik modülünü ise %85.8 oranında artırmıştır. PA6-5CB-15CE kompozitine ilave edilen EPDM elastomeri darbe mukavemetini %14.2 oranında, kopmadaki % uzama miktarını ise %56.2 oranında artırmıştır. Mikroyapı incelemeleri ise taramalı elektron mikroskobu (SEM) kullanılarak incelenmiştir.
  • [ X ]
    Öğe
    Cam Elyaf/EPDM/Poliamit-6 Kompozitlerin Mekanik Performansının ve Mikroyapısal Özelliklerinin Belirlenmesi
    (2022) Ünal, Hüseyin; Yetgin, Salih Hakan; Ünal, Veysel Furkan
    Poliamit-6 polimerine ilave edilen EPDM elastomeri, malzemenin çekme dayanımı ve elastiklik modülü gibi değerlerini azaltırken ilave edilen cam elyaflar kompozitin kopma uzamasını azaltmaktadır. Dolayısıyla endüstrinin talep ettiği yüksek mekanik özelliklere yani yüksek mukavemet, yüksek rijitlik ve üstün kırılma tokluğu (darbe enerjisi) gibi özelliklere sahip kompozitlerin elde edilebilmesi için elastomer ve elyaf takviyeli polimer kompozitlerin birlikte üretilmesi büyük önem arz etmektedir. Bu çalışmada, katkısız poliamit 6 (PA6) polimeri ile ağırlık olarak %8 oranında Etilen-Propilen-Dien-Monomer (EPDM) katkılı poliamit 6 (PA6-8EPDM), %10 oranında cam elyaf (CE) takviyeli poliamit 6 (PA6-10CE) ve %10 CE ve %8 oranında Etilen-Propilen-Dien-Monomer katkılı poliamit 6 (PA6-10CE-8EPDM) polimer kompozitlerin mekanik özellikleri incelenmiştir. Poliamit-6 esaslı polimer kompozitler, endüstriyel tip ikiz vidalı bir ekstrüder makinesinde önce granül formda üretilmiş sonra da mekanik test numuneleri geleneksel tip bir enjeksiyon makinesi kullanılarak basılmıştır. Çalışma sonucunda, PA6 polimerine ilave edilen %8 oranındaki EPDM çekme mukavemetini %19.3, elastiklik modülünü %41.4 oranında azaltırken darbe mukavemetini %14.1 oranında artırmıştır. PA6 polimerine ilave edilen %10 oranındaki cam elyaf ise çekme mukavemetini %23.6, elastiklik modülünü %64.8 oranında artırırken darbe mukavemetini %63,4 oranında azaltmıştır. PA6 polimerine ilave edilen %10 oranındaki CE ise kompozitin eğilme mukavemeti ve eğilmedeki elastiklik modülünü sırasıyla %67.0 ve %94.0 oranlarında artırmıştır.
  • [ X ]
    Öğe
    ÇOK DUVARLI KARBON NANOTÜP KATKILI POLİPROPİLEN NANOKOMPOZİTLERİN KURU SÜRTÜNME VE AŞINMA ÖZELLİKLERİ ÜZERİNE YÜK VE KAYMA HIZININ ETKİLERİNİN İNCELENMESİ
    (2020) Yetgin, Salih Hakan
    Bu çalışmada, uyumlaştırıcı kullanılmadan ağırlıkça %0.1, %0.2, %0.3, %1 ve %2oranlarında çok duvarlı karbon nanotüp (ÇDKNT) katkılı Polipropilen (PP)nanokompozitlerinin tribolojik özellikleri incelenmiştir. PP nanokompozitler iki aşamalıergiyik kalıplama prosesi ile üretilmiştir. İlk aşamada, çift vidalı ekstruderde PPnanokompozit granüller hazırlanmıştır. Granüller hızlı bir şekilde soğutulmuştur. İkinciaşamada, nanokompozit granüller triboloji test numunelerini üretmek için enjeksiyonkalıplama tekniği ile kalıplanmıştır. ÇDKNT katkılı PP nanokompozitlerin aşınma vesürtünme davranışları 0.8, 1.2m/s, ve 1.6m/s kayma hızı ve 10, 20, 30 ve 40N yük altındakuru ortam şartlarında pim-disk sistemi kullanılarak gerçekleştirilmiştir. En düşüksürtünme katsayısı 0.8m/s kayma hızında ve 10N yük altında 2ÇDKNT polimerinde 0.393değeri ile elde edilmiştir. PP polimerine ilave edilen ÇDKNT ve artan ÇDKNT miktarınabağlı olarak aşınma oranının azaldığı belirlenmiştir. 0.1ÇDKNT, 0.2ÇDKNT, 0.3ÇDKNT,1ÇDKNT ve 2ÇDKNT nanokompozitlerin aşınma direnci katkısız PP polimerine göresırasıyla %18, %31, %50, %94 ve %233 oranlarında daha yüksek elde edilmiştir.
  • [ X ]
    Öğe
    Determination of mechanical performance of boric acid filled polypropylene based polymer composites
    (2023) Ünal, Hüseyin; Yetgin, Salih Hakan; Köse, Sinan
    Polypropylene (PP) polymer, which is one of the indispensable materials of our daily life and stands out with its lightness, low cost and chemical resistance properties in the industry, was used. In industrial applications where the properties of polymers without additives are not sufficient, composite materials are produced by adding some additives to the polymer. In this experimental study, the mechanical properties of composites produced by adding boric acid (BA) to PP polymer at 5 wt.% (PP/5BA), 10 wt.% (PP/10BA) and 15 wt.% (PP/15BA) ratios were investigated. the effect of both BA filler and optimum BA filler ratio on mechanical properties were investigated. In the production of PP/BA composites, granules were first produced in an industrial twin screw extruder. Then, PP/BA composite tensile and impact test specimens were moulded on a conventional injection moulding machine. As a result, it was observed that the tensile modulus, tensile and yield strength of the composite materials decreased with increasing boric acid filler content in PP polymer. Depending on the boric acid filler content, the tensile strength decreased by an average of 18.3% and the breaking strength decreased by 14.8%. The lowest tensile modulus was obtained with a value of 2713 MPa at 10wt.% boric acid filler addition. The impact strength increased slightly at 5 wt.% boric acid filler addition and decreased at 10wt.% and 15wt.% boric acid filler addition.
  • [ X ]
    Öğe
    Determination of the Effect of Sliding Speed on Tribological Performances of Carbon Fiber Reinforced, Graphite and PTFE Filled Poly-ether-ether-ketone (PEEK) Polymer Composite
    (Konya Teknik Univ, 2022) Maslavi, Ahmet; Unal, Huseyin; Yetgin, Salih Hakan
    Machine elements such as plastic-based bearings, rollers and bushings are used in machines used in different industrial sectors. The sliding speed and carrying loads of the machine elements in these applications determine the life of the material. In this experimental study carbon fiber reinforced and graphite and poly-tetra-flour-ethylene (PTFE) filled poly-ether-ether-ketone (HPV-PEEK) polymer, which is among the high performance engineering plastics used in bearings, rollers and bushings were used to determine tribological performances. AISI 304 stainless steel counter disc was used in the tests, the experiments were carried out under dry sliding conditions and at room temperature. Tribological tests were carried out on a pin-on-disc wear test machine under 3.53 MPa and at low (1.0 m/s) and high (4.0 m/s) sliding speeds. According to the wear test results, the friction coefficient decreased while wear rate values increased with the increase in sliding speed values. In general, the friction coefficient was obtained between 0.14 and 0.19, while the specific wear rate varied between 1.66x10(-6) and 0.48x10(-6) mm(3)/Nm. While abrasive wear mechanism was observed in HV-PEEK polymer at low sliding speed values, adhesive wear mechanism was observed at high sliding speed values.
  • [ X ]
    Öğe
    Effect of silicone, molybdenum disulfide, and multi-walled carbon nanotube on the tribological, mechanical, and thermal properties of polyamide 66/carbon fibre composites
    (Elsevier, 2025) Ozsarikaya, Bilal; Yetgin, Salih Hakan; Durmus, Ali; Calis, Fatih
    The effect of silicone, molybdenum disulfide (MoS2), and multiwalled carbon nanotubes (MWCNT) on the mechanical, thermal, and tribological characteristics of polyamide 66 (PA66) composites reinforced with carbon fibre (CF) was extensively examined in this paper. An injection molding machine was used to make test samples for mechanical, thermal, and tribological testing after the twin-screw extruder was used to create the composite materials. To evaluate the mechanical behaviours of PA66 and composite samples, tensile strength (TS) and flexural strength (FS), tensile modulus (TM) and flexural modulus (FM), elongation at break (EB), and impact strength were measured. The TS and TM of PA66/30CF increased by 89.6 % and 374.3 % compared with PA66. PA66/30CF/0.5MWCNT nanocomposites exhibited better tensile (strength of 196.5 and modulus of 23575 MPa, respectively) and flexural (strength of 289 and modulus of 17700 MPa, respectively) properties. DSC analysis indicated that the melting temperature (Tm) of PA66 composites was not affected by adding CF, MWCNT, MoS2 and silicone. In contrast, composites' crystallisation temperature (Tc) and degree of crystallinity (Xc%) values were higher than those of PA66. The addition of MWCNT, MoS2 and silicone yielded a further increase in Xc, and with 42.4 %, the PA66/30CF/0.5MWCNT/3MoS2 nanocomposite yielded the highest value. The test for pin-ondisk (PoD) wear was conducted under dry sliding conditions, with 0.4, 0.8, and 1.2 m/s of sliding velocity, and a load of 20, 30, and 40 N. The tribological measurements implied that the PA66 composites prepared with 30 wt% of CF, 0.5 wt% MWCNT and 3 wt% MoS2 showed the best friction and wear behavior. The COF of PA66 polymer was around 0.4, while the COF of PA66/CF composites was between 0.25-0.35. The incorporation of MWCNT, MoS2, and silicone into the PA66/30CF composite led to a further decrease in the COF, yielding values ranging between 0.15 and 0.25. It has been deduced that the MWCNT and MoS2 additives improved the service life and thermomechanical durability of PA66 in a distinguishable manner. It was also revealed that the composite reinforced with MWCNT and MoS2 exhibited enhanced wear resistance due to the strong interfacial bonding.
  • [ X ]
    Öğe
    Elektrik Kontak Kesicilerde Kullanabilmek için Aşınma Dirençli Polimer ve Polimer Kompozit Malzemelerin Belirlenmesi
    (2020) Ünal, Hasan Hüseyin; Yetgin, Salih Hakan
    Bu çalışma, elektrik sektöründe kontak kesicilerde aşınma direnci en iyi olan malzeme çiftini belirlemek için yapılmıştır. Aşınma deneyleri için pim-disk aşınma test cihazı kullanılmıştır. Bunun için çalışmada, disk malzemesi olarak %25 oranında uzun cam elyaf takviyeli ve %40 kalsiyum karbonat katkılı doymamış polyester esaslı termoset kompozit malzeme (%25CE+%40CaCO3+UPET) kullanılmıştır. Pim malzemeler olarak ise, katkısız poli-eter-sülfon (PES) polimeri, stiren-butadien-stiren elastomer katkılı ve %30 cam elyaf takviyeli poli-fenilen-eter (PPE+SBS+%30CE) kompoziti ve %15 cam elyaf takviyeli poli-butilen-tereftalat/poli-etilen-tereftalat karışımı kompozit (PBT/PET+%15CE) malzemelerikullanılmıştır. Tribolojik deneyler, kuru kayma şartları altında ve oda sıcaklığında gerçekleştirilmiştir. Deneyler, 0,707, 1,415, 2,123 ve 3,538 MPa basınç altında ve 0,5 m/s kayma hızında yapılmıştır. Aşınma ve sürtünme deneyleri sonucunda, malzemelerin sürtünme katsayısı ve spesifik aşınma hızları belirlenmiştir. Gerçekleştirilen deneyler sonucunda, en yüksek aşınma hızı katkısız PES polimerinde elde edilirken en düşük aşınma hızı ise PPE+SBS+%30CE kompozitinde elde edilmiştir. Gerçekleştirilen deneyler sonucunda kontak kesicilerde kullanmak için PPE+SBS+%30CE/%25CE+%40CaCO3+UPETtermoset kompozit çifti en uygun malzeme çifti olarak belirlenmiştir.
  • [ X ]
    Öğe
    Etiliden Norboren (ENB) Oranın Etilen-Propilen-Dien-Monomer (EPDM) Kauçuğun Mekanik, Reolojik ve Fiziksel Özelliklerine Etkisinin İncelenmesi
    (Çankırı Karatekin Üniversitesi, 2023) Çiftçi, Suzan; Köprü, İlker; Yetgin, Salih Hakan
    Bu çalışmada, EPDM kauçuğundaki ENB oranının mekanik, reolojik ve fiziksel özelliklere etkisi incelenmiştir. Etilen oranı %44 olan %5.5 ve %9 ENB oranına sahip EPDM kauçukları ile etilen oranı %57 olan %4.5 ve %8.9 ENB oranına sahip EPDM kauçukları üretilerek ENB oranın etkileri araştırılmıştır. Üretimler 1.5 lt’lik laboratuvar tipi mini banbury kullanılarak gerçekleştirilmiştir. Elde edilen EPDM karışımları preste 180 oC ve 20 dakika boyunca vulkanize edilerek test plakaları elde edilmiştir. Pres öncesi reometre (MDR) ve Mooney viskozite testleri ile EPDM karışımlarının reolojik ve akışkanlık özellikleri incelenmiştir. Kopma mukavemeti ve kopma uzaması gibi mekanik özelliklerin belirlenmesi için çekme testi ve ayrıca kalıcı deformasyon testi, fiziksel özelliklerin belirlenmesi için yoğunluk ve sertlik testleri yapılmıştır. Çalışma sonucunda, ENB miktarının artması ile ML ve MH, mooney viskozite ve CRI değerlerinin arttığı gözlenmiştir. Etilen oranı %44 olan numunelerde kopma mukavemeti %8.9 oranında azalırken Etilen oranı %57 olan numunelerde kopma mukavemeti %29.5 oranında artmıştır. ENB oranının artması ile kalıcı deformasyon oranı %15.2 ve %26.2 oranlarında azalmıştır.
  • [ X ]
    Öğe
    Evaluating the Effectiveness of Panoptic Segmentation Through Comparative Analysis
    (2024) Sara, Cahide; Daşdemir, İlhan; Yetgin, Salih Hakan
    Image segmentation method is extensively used in the fields of computer vision, machine learning, and artificial intelligence. The task of segmentation is to distinguish objects in images either by their boundaries or as entire objects from the entire image. Image segmentation methods are implemented as instance, semantic, and panoptic segmentation. In this article, the panoptic segmentation method, seen as an advanced stage of instance and semantic segmentation, has been applied to three datasets and compared with the instance segmentation method. Experimental results are presented visually. Numerical results have been analyzed with the Panoptic Quality (PQ) and Semantic Quality (SQ) metrics. It has been observed that the segmentation outcome was best for the CityScapes dataset for panoptic segmentation.
  • [ X ]
    Öğe
    GRAFİT KATKILI SİKLO-OLEFİN KOPOLİMER (COC) KOMPOZİTLERİN TRİBOLOJİK ÖZELLİKLERİNİN İNCELENMESİ
    (2021) Kılınç, İbrahim; Yetgin, Salih Hakan
    Bu çalışmada, ağırlıkça %5, %15, %30, %45, %60 ve %75 oranlarında grafit katkılı siklo-olefin kopolimer (COC) kompozitleri ekstrüzyon ve basınçlı kalıplama yöntemleri ile üretilmiştir. Sürtünme ve aşınma deneyleri, disk üzerinde pim sistemi (pim-disk) ile kuru ortam şartlarında, 20 N, 30 N ve 40 N yük ve 0.5 m/s, 1.0 m/s ve 1.5 m/s kayma hızında gerçekleştirilmiştir. COC polimeri ve grafit katkılı COC kompozitlerin artan kayma hızı ve yüke bağlı olarak sürtünme katsayısı azalmış aşınma oranı ise artmıştır. En düşük sürtünme katsayısı ve aşınma oranı %75 grafit katkılı COC kompozitinde elde edilmiştir. COC polimerine eklenen %75 oranındaki grafit katkısı ile sürtünme katsayısı %87.7 oranında, aşınma oranı ise %498.79 oranında azalmıştır.
  • [ X ]
    Öğe
    HİGROSKOPİK MADDELERİN ÜRETİMİNDE KULLANILABİLİR SICAKLIK, BASINÇ VE KARIŞTIRMA KONTROLLÜ ULTRASONİK PİLOT REAKTÖR TASARIMI
    (2023) Köse, Sinan; Ulusal, Fatma; Yetgin, Salih Hakan
    Çinko klorür, sodyum hidroksit, magnezyum oksit, kalsiyum oksit gibi maddeler kimyasal yapıları gereği kristalleri içerisine difüzyon/absorpsiyon gibi yollarla su tutarlar. Bu maddeler, higroskopik maddeler olarak adlandırılıp sıvı ve katılar maddelerden su uzaklaştırmak amacıyla kullanılmaktadır. Üretimleri amacıyla özel kapalı sistemler kullanılması gerekmekle birlikte ortama giren veya maddenin absorpladığı suyun ortamdan uzaklaştırılması ve kalsinasyon işlemleri için yüksek sıcaklıklarda tepkime odaları gerekmektedir. Higroskopik maddelerin tepkimesi sırasında ortaya çıkan gazların ortamdan uzaklaştırılması veya ürünün nemlenmesi önlemek için su buharının sistemden uzaklaştırılması gerekmektedir. Piyasada yer alan reaktörler incelendiğinde başta topaklanma, hantal yapıları, yüksek enerji gereksinimleri ve paketlenme süreçlerinde havayla temas gibi olumsuzluklar göstermektedirler. Bu çalışma ile kalsiyum oksit ve magnezyum oksit temel alınmak üzere, ilgili kimyasalların üretim prosesinde ve kimyasal tepkimelerinde kullanılmak amacıyla yeni bir pilot reaktör ünitesinin sınır şartlarının belirlenmesi ve 3B tasarımlarının yapılması amaçlanmıştır. Piyasada yaygın kullanımı olan reaktörler incelenerek sınır şartları belirlenmiştir. Belirlenen ihtiyaçlara göre 3 boyutlu tasarımları gerçekleştirilmiştir olup elde edilen verilere göre mevcut sistemlere göre %42 daha hafif, %50 daha küçük yeni bir sistem tasarlanmıştır. Çalışma ile en az %38 daha fazla ürün işleme kapasitesine sahip olup %25 oranında enerji kullanımını azaltan bileşenlerden oluşan yeni bir reaktörün tasarımı gerçekleşmiştir.
  • [ X ]
    Öğe
    Impact of multi-walled carbon nanotube and graphene oxide on abrasive wear performance of polypropylene
    (MIM RESEARCH GROUP, 2021) Yetgin, Salih Hakan
    In this study, the abrasive wear behavior of multi-walled carbon nanotube (MWCNT) and graphene oxide (GO) filled polypropylene (PP) nanocomposites without using compatibiliser were investigated. The effects of material type, sliding distance, and emery paper number on the abrasive wear of PP nanocomposites were investigated by adopting a statistical approach. The tribological tests were performed in dry condition using pin-on-disc at 1.0m/s sliding speed and 10N load. The optimization of signal-to-noise ratio (S/N) and degree of significance of the control variables to minimize the wear volume and coefficient of friction was carried out. As a result of the study, wear volume and coefficient of friction increased with increasing sliding distance, while decreased with increasing emery paper number for all tested materials. The coefficient of friction of the MWCNT and GO filled PP nanocomposites decreased by 19% and 23% compared to unfilled PP polymer, respectively. GO filled PP nanocomposites was found to be approximately 95% less wear volume than MWCNT filled PP nanocomposites. The minimized coefficient of friction and wear volume was obtained at 0.3%wt GO filled PP nanocomposite with the parameters of 100m sliding speed and 1200 grid emery paper number with a value of 0.2716 and 3.07 mm3, respectively. © 2021 MIM Research Group. All rights reserved.
  • [ X ]
    Öğe
    INVESTIGATION OF DRILLING PERFORMANCE OF REINFORCED POLYAMIDE 6 POLYMER COMPOSITE
    (Konya Teknik Univ, 2023) Genc, Abdurrahman; Yildirim, Ferhat; Koyunbakan, Murat; Yetgin, Salih Hakan; Eskizeybek, Volkan; Kus, Gozde
    Polyamides are preferred polymer materials for manufacturing industrial products due to their lightness, resistance to corrosion, ease of processing, and recyclability. In this study, the machinability properties of Polyamide 6 (PA6) polymer composite plates reinforced with chopped carbon fiber (CF) and multi-walled carbon nanotube (MWCNT) in different proportions were investigated by the drilling method using different cutting tools and cutting parameters. The experiments were carried out according to the L16 orthogonal array. Drilling experiments were carried out in a dry environment. The deformations occurring on the inlet and outlet surfaces of the drilled samples were calculated, and the surface roughness (Ra) of the hole walls was measured. According to the results obtained, the particle addition made to the PA6 polymer reduced the Ra. It has been observed that high cutting speed and low feed rate are ideal parameters to achieve low Ra and low inlet-outlet deformations.
  • [ X ]
    Öğe
    Investigation of Physical and Mechanical Properties of Ethylene Propylene Diene Monomer (EPDM) and Styrene Butadiene Rubber (SBR) with Sulfur and Peroxide Vulcanization
    (Türk Eğitim-Sen, 2023) Öteleş, Ali; Köprü, İlker; Yetgin, Salih Hakan
    In this study, Styrene Butadiene Rubber (SBR) and Ethylene Propylene Diene Monomer (EPDM) rubbers were produced by Sulfur and Peroxide vulcanization methods and their physical and mechanical properties were examined. EPDM and SBR were turned into dough using a 1,5-liter laboratory type mini bandury. The obtained materials was vulcanized in the press at 180 °C for 20 minutes, and test plates were obtained. Rheological and fluidity properties of EPDM and SBR rubbers were examined using pre-press rheometer (MDR) and Mooney viscosity tests. Tensile tests and permanent deformation tests were performed to determine mechanical properties and density and hardness tests were performed to determine physical properties. As a result of the study, CRI values increased by 52,2% for EPDM/P rubber and 2,8% for SBR/P rubber. While the Mooney density value of EPDM/P and EPDM/K rubbers did not change, it decreased by 16,7% of SBR/P rubber. Depending on the vulcanization type of EPDM rubber, the breaking strength and elongation at break increased, while the breaking elongation of SBR rubber decreased. While the compression set of EPDM/P rubber increased by 86,9%, the compression set of SBR/P rubber decreased by 78,1%.