    Characterization of biodegradable films based on guar gum and calcium caseinate incorporated with clary sage oil: Rheological, physicochemical, antioxidant, and antimicrobial properties
    (Elsevier, 2024) Bhatia, Saurabh; Shah, Yasir Abbas; Al-Harrasi, Ahmed; Alhadhrami, Aysha Salim; Alhashmi, Dalal Sulaiman Hamed; Jawad, Muhammad; Diblan, Sevgin
    Clary sage essential oil (CSEO) has been reported for its wide food and pharmaceutical applications. This work aimed to produce biodegradable active guar gum-calcium caseinate (GG-CC) based film incorporated with CSEO and to evaluate its physico-chemical, antioxidant, and antibacterial properties. Solvent casting technique was used to prepare the composite films containing CSEO at 0.1, 0.15, and 0.2% (v/v). The chemical, rheological, morphology, mechanical, thermal, optical, crystalline, biodegradable, water barrier, antioxidant and antimicrobial potential of the samples were assessed by various analytical methods. Rheological findings of filmogenic solution revealed that the viscosity of filmogenic solutions (GCEO2-GCEO4) increased with an increase in the concentration of the CSEO. CSEO addition in GG-CC film exhibited a homogenous structure with low crystallinity, transparency, water vapor permeability, moisture content, and tensile strength values, whereas a rise in elongation at break, thickness, and thermal stability was observed. Fourier transforms infrared (FTIR) results suggested the interaction between CSEO and GG-CC-CSEO films also exhibited satisfactory antioxidant activity against DPPH and ABTS free radicals and higher antimicrobial effect against the Gram-negative bacteria (Pseudomonas aeruginosa). This work revealed that CSEO has the potential to be used as an active ingredient in the development of films for food packaging applications.
  • [ X ]
    Öğe
    Impregnation of Pectin-Sodium Caseinate Films with Lemongrass Essential Oil: Physical-Chemical, Antimicrobial, and Antioxidant Assessment
    (Amer Chemical Soc, 2024) Bhatia, Saurabh; Khan, Talha Shireen; Alhadhrami, Aysha Salim; Shah, Yasir Abbas; Philip, Anil K.; Diblan, Sevgin; Koca, Esra
    Biopolymers derived from natural resources have gained much interest in the past few decades to replace conventional nonbiodegradable petroleum-based packaging. Essential oils and plant extracts are frequently utilized for their antimicrobial and antioxidant properties in the development of edible films and coatings serving as bioactive compounds. The current study investigated the impact of various concentrations of lemongrass essential oil (LEO) on the physical and chemical characteristics as well as the antioxidant capabilities of films made from sodium caseinate and pectin. The addition of LEO led to a decrease in mechanical parameters of film samples like elongation at break (EAB) decreased from 19.73 +/- 0.81 to 4.06 +/- 0.20 and tensile strength (TS) decreased from 11.16 +/- 0.81 to 2.43 +/- 0.08 but a rise in opacity (4.39 +/- 0.14 to 5.60 +/- 0.13), thickness (0.044 +/- 0.005 to 0.078 +/- 0.005), and water vapor permeability (WVP) (0.391 +/- 0.013 to 0.760 +/- 0.035) was observed. The gloss value of the film samples increased from 11.9 +/- 0.1 to 13.1 +/- 0.1, and haziness increased from 45.85 +/- 1.05 to 71.69 +/- 0.25 as the concentration of LEO increased, reducing their transparency (89.22 +/- 0.27-88.24 +/- 0.19). Scanning electron microscopy (SEM) revealed additional microstructural alterations in the films as a result of the addition of LEO. Furthermore, antimicrobial activity was detected in the PSC4 film sample against E. coli. The oil-loaded films showed significantly higher antioxidant activity of 40.41% compared to the control film sample, having 16.57% antioxidant activity. Contact angle measurements demonstrated that the film samples became more hydrophobic with the addition of LEO (55.52 degrees in the maximum LEO concentrated film). This study introduces a promising method for creating active food packaging materials for packaging applications.